Novel Free Layer Structure in Magnetic Random Access Memory (MRAM) for Mo or W Perpendicular Magnetic Anisotropy (PMA) Enhancing Layer

ABSTRACT

A perpendicularly magnetized magnetic tunnel junction (p-MTJ) is disclosed wherein a free layer (FL) has a first interface with a MgO tunnel barrier, a second interface with a Mo or W Hk enhancing layer, and is comprised of Fe x Co y B z  wherein x is 66-80, y is 5-9, z is 15-28, and (x+y+z)=100 to simultaneously provide a magnetoresistive ratio &gt;100%, resistance x area product &lt;5 ohm/μm 2 , switching voltage &lt;0.15V (direct current), and sufficient Hk to ensure thermal stability to 400° C. annealing. The FL may further comprise one or more M elements such as 0 or N to give (Fe x Co y B z ) w M 100-w  where w is &gt;90 atomic %. Alternatively, the FL is a trilayer with a FeB layer contacting MgO to induce Hk at the first interface, a middle FeCoB layer for enhanced magnetoresistive ratio, and a Fe or FeB layer adjoining the Hk enhancing layer to increase thermal stability.

RELATED PATENT APPLICATIONS

This application is related to the following: U.S. Pat. Nos. 8,372,661; 9,472,752; and 9,780,299; which are assigned to a common assignee and herein incorporated by reference in their entirety.

TECHNICAL FIELD

The present disclosure relates to a perpendicularly magnetized magnetic tunnel junction (p-MTJ) comprised of a free layer that has a first interface with a tunnel barrier layer and a second interface with a metal PMA (Hk) enhancing layer such as Mo or W that increases PMA and thermal stability in the free layer while reducing a resistance x area (RA) product compared with a p-MTJ having a metal oxide Hk enhancing layer, and optimizing a figure of merit A where A is the product of Hk and the magnetoresistive (MR) ratio in order to satisfy magnetic performance requirements for advanced MRAM products.

BACKGROUND

Perpendicularly magnetized MTJs (p-MTJs) are a major emerging technology for use in embedded magnetic random access memory (MRAM) applications, and standalone MRAM applications. P-MTJ MRAM technology that uses spin-torque (STT-MRAM) for writing of memory bits was described by C. Slonczewski in “Current driven excitation of magnetic multilayers”, J. Magn. Magn. Mater. V 159, L1-L7 (1996), and is an increasingly promising candidate for future generations of non-volatile memory to replace embedded flash memory and embedded cache memory (SRAM).

Both MRAM and STT-MRAM have a p-MTJ cell based on a tunneling magnetoresistance (TMR) effect wherein a stack of layers has a configuration in which two ferromagnetic layers are separated by a thin insulating tunnel barrier layer such as MgO. One of the ferromagnetic layers called the pinned layer has a magnetic moment that is fixed in an out-of-plane direction such as the +z direction when the plane of each layer is laid out in the x-ax is and y-ax is directions. The second ferromagnetic layer has an out-of-plane magnetization direction that is free to rotate to either the +z-ax is (parallel or P state) or the −z-ax is (antiparallel or AP state) direction. The difference in resistance between the P state (Rp) and AP state (Rap) is characterized by the equation (Rap-Rp)/Rp also known as DRR or the MR ratio. It is important for p-MTJ cells to have a large MR ratio, preferably higher than 100%, as the MR ratio is directly related to the read margin for the memory bit, or how easy it is to differentiate between the P state and AP state (0 or 1 bits).

Another critical requirement for p-MTJs is thermal stability during 400° C. process temperatures that are typical of back-end-of-line (BEOL) processes when fabricating embedded memory devices in complementary metal-oxide-semiconductor (CMOS) products. A general trend has been to introduce a second metal oxide/free layer (FL) interface similar to the tunnel barrier/FL interface thereby enhancing PMA and Hk within the free layer, and improving thermal stability. Unfortunately, a consequence of employing a Hk enhancing (cap) layer such as MgO on the free layer is the addition of parasitic resistance to the p-MTJ. Equation (1) shows the effect of the cap layer resistance contribution to total p-MTJ resistance while Equation (2) indicates the impact on DRR (MR ratio).

$\begin{matrix} {{{DRR} = {\frac{R_{AP} - R_{P}}{R_{P}}\mspace{14mu} {where}}}{R_{AP} = {R_{AP}^{barrier} + {R_{AP}^{cap}\mspace{14mu} {and}}}}{R_{P} = {R_{P}^{barrier} + R_{P}^{cap}}}{{{Since}\mspace{14mu} R_{AP}^{cap}} = R_{P}^{cap}}} & {{Eq}.\mspace{14mu} (1)} \\ {{DRR} = {\frac{R_{AP}^{barrier} + R_{AP}^{cap} - \left( {R_{P}^{barrier} + R_{P}^{cap}} \right)}{R_{P}^{barrier} + R_{P}^{cap}} = \frac{R_{AP}^{barrier} - R_{P}^{barrier}}{R_{P}^{barrier} + R_{P}^{cap}}}} & {{Eq}.\mspace{14mu} (2)} \end{matrix}$

In summary, the series resistance (R_(AP) ^(cap) and R_(P) ^(cap)) caused by the metal oxide cap layer will cause a reduction in DRR, unfortunately reducing the MRAM bit reading margin as well as increasing the bit's writing voltage by adding a series resistance. Therefore, an alternative p-MTJ cell structure is needed that features a RA product preferably less than 5 ohm-μm² for advanced memory products while achieving an acceptable Hk (PMA) for enhanced thermal stability, and increasing the MR ratio above 100% while minimizing switching voltage (Vc).

SUMMARY

One objective of the present disclosure is to reduce the switching voltage and resistance x area (RA) product for p-MTJ cells while optimizing Hk and the MR ratio to provide the overall magnetic performance necessary to satisfy requirements for advanced embedded memory products.

A second objective is to provide a method of forming the p-MTJ of the first objective that is readily implemented in embedded memory devices found in CMOS products.

According to one embodiment of the present disclosure, a p-MTJ configuration is provided where a free layer is formed between a metal oxide tunnel barrier layer and a metal Hk enhancing layer such as W or Mo in order to minimize the RA product, and increase the MR ratio by removing the R_(P) ^(cap) contribution to equation (2) described previously. The p-MTJ may have a bottom spin valve configuration with the tunnel barrier layer below the free layer, or a top spin valve configuration with the free layer below the tunnel barrier layer.

The free layer may be a single layer as deposited and comprises at least Fe, Co, and B. In some embodiments, one or more additional elements (M) such as oxygen, nitrogen or a metal from an adjacent layer diffuse into the free layer during p-MTJ fabrication to give a final free layer composition that is (Fe_(x)Co_(y)B_(z))_(w)M_(100-w) where x is 66-80, y is 5-9, z is 15-28, x+y+z=100, and w>90 atomic %. Moreover, the free layer thickness is preferably from 8 to 15 Angstroms to realize a small switching voltage (V_(C))<0.15V (direct current or DC) since V_(C) is proportional to the magnetization volume of the free layer. It is believed that a certain degree of segregation occurs during one or more annealing steps after the MTJ stack of layers is formed so that the final p-MTJ structure may have a free layer with a FeB/FeCoB or FeCoB/FeB bilayer configuration, or even a FeB/FeCoB/FeB or FeB/FeCoB/Fe trilayer stack where a lower layer contacting the tunnel barrier has a FeB composition, a middle portion maintains a FeCoB composition, and an upper layer contacting the Hk enhancing layer in a bottom spin valve embodiment has a Fe or FeB composition. When one or more M elements are present, M may be unevenly dispersed within the free layer depending on the atomic number of M and the bond strength of an M atom with the other atoms in the free layer.

According to a second embodiment, a free layer has a trilayer stack as deposited and is formed with a FeB/FeCoB/Fe or FeB/FeCoB/FeB configuration between a tunnel barrier and a Mo or W Hk enhancing layer. In other words, a first layer that contacts the tunnel barrier is comprised of Fe and B. In particular, when the tunnel barrier is MgO, a MgO/FeB interface provides enhanced Hk compared with a MgO/CoFeB interface, for example. However, a free layer consisting only of FeB does not meet the objectives of the present disclosure since a high MR ratio is not realized simultaneously with enhanced Hk. Therefore, a certain amount of Co is employed in the iron rich FeCoB middle layer. Since Co has a lower affinity for oxygen than Fe, Co is advantageously used in the middle portion of the free layer to block oxygen migration from the tunnel barrier layer to the third layer (Fe or FeB) thereby maintaining Hk that results from the third layer interface with the W or Mo Hk enhancing layer. The addition of Co to a FeB alloy also enhances the MR ratio. Furthermore, the trilayer thickness is preferably from 8 to 15 Angstroms so that Vc is minimized. A total composition of the trilayer structure is (Fe_(x)Co_(y)B_(z)) where x is 66-80, y is 5-9, z is 15-28, and x+y+z is 100, or the (Fe_(x)Co_(y)B_(z))_(w)M_(100-w) composition described earlier wherein w>90 atomic % when one or more M elements are incorporated into the trilayer during p-MTJ fabrication.

Another key feature of the trilayer embodiment is that the third layer portion contacting the Mo or W Hk enhancing layer must be Fe or Fe-rich material to minimize or avoid a dead zone. Otherwise, for the case of alloys such as CoFeB, there is intermixing with the Mo or W layer that results in a dead zone with substantially reduced PMA. Thus, a Fe or Fe-rich FeB layer has essentially no intermixing with W or Mo and thereby provides a maximum Hk contribution to PMA within the free layer from the Fe/Hk enhancing layer interface or from the FeB/Hk enhancing layer interface.

The present disclosure also encompasses a method of forming a free layer between a tunnel barrier and a W or Mo Hk enhancing layer wherein the free layer is formed in multiple steps. In one embodiment, a first layer comprised of Fe and B is deposited on the tunnel barrier layer. Then, a FeCoB layer that comprises more Co than in the first layer is deposited to give a FeB/FeCoB stack, for example. Thereafter, a third layer is deposited on the FeCoB layer and is FeB or Fe having a Fe content that is greater than the Fe content in the FeCoB layer. After a W or Mo Hk enhancing layer is deposited on the free layer, and optionally a hard mask on the W or Mo layer, the p-MTJ stack is annealed at a temperature >380° C. The annealing may comprise one or more steps that occur before or after the p-MTJ stack of layers is patterned into a plurality of p-MTJ cells.

In an alternative embodiment, a Fe_(x)Co_(y)B_(z) single layer is deposited on the tunnel barrier layer, and then a W or Mo Hk enhancing layer is formed on the Fe_(x)Co_(y)B_(z) free layer. After an optional hard mask is deposited, the resulting MTJ stack of layers is annealed at a temperature >380° C. thereby causing segregation in the Fe_(x)Co_(y)B_(z) free layer to yield a free layer that is a FeB/FeCoB or FeCoB/FeB bilayer, or that is a trilayer with a FeB/FeCoB/Fe or FeB/FeCoB/FeB configuration.

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross-sectional view showing a p-MTJ wherein a free layer is formed between a tunnel barrier layer and a Mo or W Hk enhancing layer in a bottom spin valve configuration according to an embodiment of the present disclosure.

FIG. 2 is a cross-sectional view showing a p-MTJ wherein a free layer is formed between a Mo or W Hk enhancing layer and a tunnel barrier layer in a top spin valve configuration according to another embodiment of the present disclosure.

FIG. 3 depicts a p-MTJ previously fabricated by the inventors wherein a CoFeB layer is formed between a MgO tunnel barrier and a Mo cap layer, which results in an intermixing layer.

FIG. 4 is a cross-sectional view of a p-MTJ wherein the free layer is a CoFeB/FeB bilayer to substantially reduce or avoid the intermixing layer at an interface with an overlying Mo layer.

FIG. 5 is a cross-sectional view of a p-MTJ wherein a Fe_(x)Co_(y)B_(z) free layer is formed between a MgO tunnel barrier and a Mo Hk enhancing layer, and may segregate to a FeCoB/FeB or FeB/FeCoB bilayer during annealing according to a first embodiment of the present disclosure.

FIGS. 6A-6B are cross-sectional views of a p-MTJ with a bottom spin valve and top spin valve configuration, respectively, wherein a free layer with a FeB/FeCoB/Fe or FeB/FeCoB/FeB trilayer configuration and a total composition equivalent to Fe_(x)Co_(y)B_(z) is formed between a MgO tunnel barrier and a Hk enhancing layer according to a second embodiment of the present disclosure.

FIGS. 7-8 are phase diagrams for Co—Mo and Fe-Mo, respectively, that indicate solubility of Co in Mo, and insolubility of Fe with Mo at CMOS process temperatures.

FIG. 9 is a bar chart that shows a comparison of free layer compositions previously fabricated by the inventors with embodiments of the present disclosure with regard to a figure of merit A where A is the product of Hk and MR ratio.

FIG. 10 is a ternary plot of Fe, Co, and B composition showing the free layer composition region represented by the embodiments of the present disclosure, and outlying regions typical of the prior art.

FIGS. 11-13 show a sequence of steps used to fabricate a p-MTJ according to an embodiment of the present disclosure.

FIG. 14 is a flow diagram depicting a series of steps where a Fe_(x)Co_(y)B_(z) free layer is formed between a tunnel barrier layer and Mo or W Hk enhancing layer in a p-MTJ stack of layers.

DETAILED DESCRIPTION

The present disclosure is related to p-MTJ cells and the fabrication thereof wherein thermal stability, MR ratio, RA product, and switching voltage are simultaneously optimized for embedded memory applications. A key feature is a free layer comprised of Fe_(x)Co_(y)B_(z) where x is 66-80, y is 5-9, and z is 15-28, and x+y+z=100, and the free layer forms a first interface with a tunnel barrier layer and a second interface with a Mo or W Hk enhancing layer in a p-MTJ. In some embodiments, one or more elements M may diffuse into the free layer during p-MTJ fabrication to give a (Fe_(x)Co_(y)B_(z))_(w)M_(100-w) composition where w>90 atomic %. The p-MTJ may be incorporated in a MRAM, STT-MRAM, or another spintronic device such as a spin torque oscillator (STO), sensor, or biosensor. Only one p-MTJ cell is depicted in the drawings, but typically millions of p-MTJ cells are arrayed in rows and columns on a substrate during fabrication of a memory device. A top surface for a layer is defined as a surface facing away from the substrate while a bottom surface faces the substrate. An interface is a boundary region comprised of a bottom surface of one layer and an adjoining top surface of a second layer. A thickness of each layer is in the z-ax is direction, and a plane (top or bottom surface) is laid out in the x-ax is and y-ax is directions.

For advanced technology nodes, especially for MRAM and STT-MRAM cells having a critical dimension (CD) <60 nm, there is a difficult challenge to simultaneously satisfy important requirements including thermal stability to 400° C. process temperatures, MR ratio above 100%, RA product <5 ohm-μm², and switching voltage <0.15V (DC), and preferably <0.1V (DC). P-MTJ cell improvements in the prior art address two or at most three of the aforementioned requirements but fail to satisfy all four of these performance needs. The present disclosure provides a solution to meet all of the aforementioned requirements. However, the present disclosure is not limited to high-end memory devices and also provides the simultaneous benefits of 400° C. thermal stability, MR ratio >100%, and switching voltage <0.15V (DC) for applications where an RA product >5 ohm-μm² is acceptable.

In related U.S. Pat. No. 8,372,661, we disclosed a Fe/CoFeB/Fe trilayer configuration for a free layer that was designed to reduce switching current. Although MR ratios above 100% were achieved, the RA product was from 8 to 10 ohm-μm² while thermal stability and Hk were not discussed. Also, in related U.S. Pat. No. 9,780,299, we disclosed that improved seed layer stacks with a higher degree of uniformity (top surface smoothness) than previously realized translate to improved thermal stability at 400° C. However, other magnetic performance related parameters were not discussed.

Now we have found that all performance requirements mentioned earlier are achieved in a p-MTJ cell comprised of a tunnel barrier/free layer/Mo or W Hk enhancing layer stack or with a Mo or W Hk enhancing layer/free layer/tunnel barrier stack, and wherein the free layer comprises Fe_(x)Co_(y)B_(z) where x is 66-80, y is 5-9, z is 15-28, and x+y+z=100.

FIG. 1 depicts a patterned p-MTJ 1 according to a first embodiment of the present disclosure wherein an optional seed layer 11, pinned layer 12, tunnel barrier layer 13, free layer 14, Hk enhancing layer 17, and hard mask 16 are sequentially formed on a top surface 10 t of a substrate that is a bottom electrode 10 in a MRAM structure, for example. Sidewall 1 s on the p-MTJ cell is formed during a conventional photoresist patterning and etching sequence where a pattern formed in a photoresist layer (not shown) on top surface 16 t of the hard mask is etch transferred through the underlying p-MTJ stack of layers as explained later. Free layer magnetization 14m is free to rotate parallel or anti-parallel to the pinned layer magnetization 12m in this bottom spin valve embodiment.

According to another embodiment of the present disclosure shown as p-MTJ 2 in FIG. 2, a top spin valve configuration is illustrated where the p-MTJ layers are retained from FIG. 1 except they are stacked in a different order. Here, the optional seed layer 11, Mo or W Hk enhancing layer 17, free layer 14, tunnel barrier 13, reference layer 12, and hard mask 16 are sequentially formed on a substrate comprised of an uppermost bottom electrode 10. The seed layer is comprised of one or more of NiCr, Ta, Ru, Ti, TaN, Cu, Mg, or other materials typically employed to promote a smooth and uniform grain structure in overlying layers. In related U.S. Pat. No. 9,780,299, we described one of the preferred seed layer configurations that is a TaN/Mg/CoFeB/NiCr stack of layers in order to provide an especially smooth top surface 11 t that improves magnetic properties in overlying layers.

Referring to FIG. 3, we have previously fabricated p-MTJ cells comprised of a MgO tunnel barrier 13, CoFeB free layer 14 x 1, and Mo Hk enhancing layer 17 having a bcc crystal structure. Although the MgO/CoFeB interface 40 generates PMA that induces magnetization 14 m 1, we observe there is intermixing between the CoFeB free layer (FL) and Mo Hk enhancing layer whereby a dead zone 20 is formed that essentially prevents PMA to be induced at the original FL/Mo interface 41. As a result, thermal stability suffers because of the lack of a second Hk contribution from interface 41 that is needed to enhance PMA in the free layer.

Referring to FIG. 4, we have modified the p-MTJ cell in FIG. 3 to include a bilayer scheme to yield a free layer 14 x 2 where an upper layer 14 b that is FeB contacts the Mo layer 17 at interface 41 to substantially reduce or prevent the intermixing region 20 a. Here, we find an additional Hk contribution (magnetization 14 m 2) that together with magnetization 14 m 1 at interface 40 provides enhanced PMA for the free layer compared with the FL structure in FIG. 3. However, due to the unoptimized composition of the lower CoFeB layer 14 a, the MR ratio for free layer 14 x 2 is generally too low to be acceptable for advanced MRAM and STT-MRAM applications.

To our knowledge, the role of the free layer composition at interface 41 with a Mo or W Hk enhancing layer 17 (also known as a cap layer in a bottom spin valve configuration) has not been previously addressed with regard to intermixing between FL 14 and the Hk enhancing layer. In particular, our observation that an uppermost Fe or FeB sub-layer in a composite free layer 14 in FIG. 1 (or a bottommost Fe or FeB sub-layer in free layer 14 in FIG. 2) prevents undesirable intermixing with Mo or W in Hk enhancing layer 17 is a key feature of the present disclosure. In other words, optimum Hk at interface 41 and sufficient PMA in free layer 14 to provide acceptable thermal stability at 400° C. process temperatures is achieved with a Fe/Mo, Fe/W, FeB/Mo, or FeB/W interface according to embodiments described herein.

The intermixing behavior in FIG. 3 and lack thereof in FIG. 4 is supported by information found in phase diagrams in the Fact Sage steel database. Referring to FIG. 7, a Co—Mo phase diagram indicates solubility (intermixing) of Mo and Co at typical CMOS process temperatures. On the other hand, in FIG. 8, a corresponding Fe-Mo phase diagram indicates essentially no intermixing of Fe with Mo at typical CMOS process temperatures.

Returning to FIGS. 1-2, reference layer 12 may have a synthetic anti-parallel (SyAP) configuration represented by AP2/Ru/AP1 where an anti-ferromagnetic coupling layer made of Ru, Rh, or Ir, for example, is sandwiched between an AP2 magnetic layer and an AP1 magnetic layer (not shown). The AP2 (outer pinned) layer is formed on the seed layer 11 in FIG. 1 or adjoins the hard mask 16 in FIG. 2. AP1 is the inner pinned layer and typically contacts the tunnel barrier. One or both of the AP1 and AP2 layers may be comprised of CoFe, CoFeB, Fe, Co, or a combination thereof. In other embodiments, one or both of the AP1 and AP2 layers may be a laminated stack with inherent PMA such as (Co/Ni)_(n), (CoFe/Ni)_(n), (Co/NiFe)_(n), (Co/Pt)_(n), (Co/Pd)_(n), or the like where n is the lamination number. Furthermore, a dusting layer that is Co or a Co rich alloy may be inserted between the AFM coupling layer and each of the AP1 and AP2 layers to yield an AP2/Co/Ru/Co/AP1 reference layer configuration with enhanced PMA and thermal stability as we disclosed in related U.S. Pat. No. 9,472,752.

Tunnel barrier layer 13 is preferably a metal oxide that is one of MgO, TiOx, AlTiO, MgZnO, Al₂O₃, ZnO, ZrOx, HfOx, or MgTaO, or a lamination of one or more of the aforementioned metal oxides. More preferably, MgO is selected as the tunnel barrier layer because it provides the highest MR ratio (DRR).

The Mo or W Hk enhancing layer 17 has a thickness from 10 to 50 Angstroms, and preferably 20 to 30 Angstroms. In some embodiments, a MoW alloy may be used as the Hk enhancing layer, or a MoD alloy or WD alloy where D is one of Nb, Ti, Ta, Zr, Hf, V, or Cr, and wherein the D content is less than 20 atomic %.

Hard mask 16 is non-magnetic and generally comprised of one or more conductive metals or alloys including but not limited to Ta, Ru, TaN, Ti, TiN, and W. It should be understood that other hard mask materials including MnPt may be selected in order to provide high etch selectivity relative to underlying MTJ layers during an etch process that forms MTJ cells with sidewalls that stop on the bottom electrode. Moreover, the hard mask may comprise an electrically conductive oxide such as RuOx, ReOx, IrOx, MnOx, MoOx, TiOx, or FeOx.

According to a first embodiment of the present disclosure shown in FIG. 5, free layer 14 has a Fe_(x)Co_(y)B_(z) composition as deposited where x is 66-80, y is 5-9, z is 15-28, and x+y+z=100. However, after one or more annealing steps during subsequent memory device fabrication, one or more M elements where M is a metal, oxygen, or nitrogen from the underlying tunnel barrier layer (or Hk enhancing layer or another adjacent layer) may diffuse into the FL to yield a (Fe_(x)Co_(y)B_(z))_(w)M_(100-w) composition where w>90 atomic %. Moreover, the Fe_(x)Co_(y)B_(z) free layer may segregate into two or more sub-layers. Thus, the present disclosure anticipates that the free layer in FIG. 1 or FIG. 2 may transform to a bilayer 14′ with a FeB/FeCoB or FeCoB/FeB configuration after annealing or exposure to process temperatures >380° C. Note that after segregation occurs, the “total” composition of the FL may be maintained as Fe_(x)Co_(y)B_(z). Hk contribution 14 m 1 at interface 40 and Hk contribution 14 m 2 at interface 41 both contribute to FL magnetization 14 m in FIG. 1 and FIG. 2.

Referring to FIG. 6A, a second embodiment of the present disclosure is depicted where free layer 14 has a trilayer configuration that is formed by sequentially depositing a FeB layer 14-1 on a tunnel barrier 13 such as MgO in a bottom spin valve p-MTJ structure, a FeCoB middle layer 14-2, and an uppermost Fe or FeB layer 14-3 where a total composition of free layer 14 is Fe_(x)Co_(y)B_(z) described previously. The Hk enhancing layer 17 such as Mo, W, or a Mo alloy or W alloy described earlier is then deposited on the uppermost Fe or FeB layer followed by a hard mask 16 depicted in FIG. 1. In a top spin valve embodiment shown in FIG. 6B, the sequence is reversed where Fe or FeB layer 14-3, FeCoB middle layer 14-2, and FeB layer 14-1 are sequentially deposited on the Hk enhancing layer. Thereafter, the tunnel barrier is formed on layer 14-1 followed by the reference layer 12 and hard mask 16 as shown in FIG. 2. As in the previous embodiment, the FL may have a (Fe_(x)Co_(y)B_(z))_(w)M_(100-w) composition if one or more M elements diffuse into one or more layers 14-1, 14-2, 14-3 during subsequent processing steps at temperatures >380° C.

The benefits of the trilayer stack for free layer 14 shown in FIGS. 6A-6B are that all four of the p-MTJ objectives of the present disclosure are simultaneously realized. In particular, when the tunnel barrier 13 is MgO, an interface 40 with FeB layer 14-1 provides enhanced Hk 14 m 1 compared with a MgO/CoFeB interface in FIG. 4, for example. However, a free layer consisting only of FeB does not meet the objectives of the present disclosure since a high MR ratio is not realized simultaneously with enhanced Hk. Therefore, a certain amount of Co is employed in the iron rich FeCoB middle layer 14-2. Since Co has a lower affinity for oxygen than Fe, Co is advantageously used in the middle portion of the free layer to block oxygen migration from the tunnel barrier layer to the Fe or FeB layer 14-3 thereby maintaining Hk 14 m 2 that results from interface 41 with the Hk enhancing layer 17. The addition of Co to a FeB alloy in middle layer 14-2 also enhances the MR ratio.

The thickness of free layer 14 is preferably from 8 to 15 Angstroms so that Vc is minimized, and a total composition of the trilayer structure should be equivalent to Fe_(x)Co_(y)B_(z) described previously. It is also important that layer 14-3 contacting the Hk enhancing layer is Fe or an Fe-rich material to minimize or avoid a dead zone having substantially reduced PMA or no PMA that results when Co or a Co alloy such as CoFeB intermixes with a W, Mo, Mo alloy, or W alloy layer. Thus, a Fe or Fe-rich FeB layer has essentially no intermixing with W, Mo, or alloys thereof and thereby provides a maximum Hk value resulting from interface 41. An Fe rich FeB layer is defined as a layer with a Fe content >50 atomic %. Preferably, the Fe content is ≥70 atomic %, and more preferably is ≥90 atomic %.

To demonstrate the benefits of the p-MTJ configurations disclosed herein, we performed an experiment to compare p-MTJ configurations having various free layers (comparative examples) formed during our past p-MTJ development projects with those formed according to the embodiments described herein. The base film structure employed for all p-MTJ stacks is TaN20/Mg7/CoFeB9/NiCr50/(Ni6/Co1.8)₃/Co5/Ru4/Co5/Mo2/CoFeB4/Fe5/MgO/free layer12/Mo20/Ta15/Ru100 where the thickness of each layer is shown in Angstroms. Total free layer thickness in each example is 12 Angstroms. In the base film structure, TaN/Mg/CoFeB/NiCr is the seed layer, (Ni/Co)₃ is the AP2 layer, the Ru AFM coupling layer is sandwiched between two Co dusting layers, the first Mo layer is a Hk enhancing layer for the overlying AP1 layer, CoFeB/Fe is the AP1 layer that adjoins the MgO tunnel barrier, the second Mo layer is the Hk enhancing layer for the FL, and Ta/Ru is the hard mask. The Mo layer next to AP1 also serves as a bridge (crystal decoupling) between the underlying Co dusting layer with a fcc(111) structure and overlying CoFeB with a bcc(002) crystal structure.

After all p-MTJ layers were deposited, each stack was annealed at 400° C. for 140 minutes to confirm thermal tolerance to typical 400° C. processes. Actual RA product results for all examples are within 3-4 ohm/μm² and thus satisfactory for advanced embedded memory products having a CD <60 nm. MR ratio and Hk were measured after annealing, and a comparison was made among stacks by using a figure of merit A where A is the product of MR ratio and Hk (in arbitrary units). A relative merit of 0 is given when A<1000, 1 is for A between 1000 and 1100, 2 is for A between 1100 and 1200, 3 is for A between 1200 and 1300, 4 is for A between 1300 and 1400, and 5 (best result) is for A above 1400.

With regard to Table 1, the most common single free layer composition in our earlier development efforts is Fe₆₀Co₂₀B₂₀ and listed as Comp. Ex. 1, and a second popular composition is Fe₇₀Co₃₀ (Comp. Ex. 2). Both have an A result below 1000. However, a single layer composition Fe₇₇Co₇B₁₆ according to Embodiment 1 improves performance significantly. Our earlier bilayer configurations are listed as Fe8/Fe₆₀Co₂₀B₂₀4 and Fe₆₀Co₂₀B₂₀4/Fe8, or Comp. Ex. 3 and Comp. Ex. 4, respectively, and show no improvement over the single layer baseline results. On the other hand, bilayer configurations according to Embodiment 1, which are represented as Fe₇₀B₃₀8/Fe₆₀Co₂₀B₂₀4, Fe₇₀B₃₀7/Fe₆₀Co₂₀B₂₀5, and Fe₆₀Co₂₀B₂₀4/Fe₇₀B₃₀8 provide A results between 1000 and 1200, a considerable improvement over prior art bilayers.

TABLE 1 P-MTJ properties with TaN20/Mg7/CoFeB9/NiCr50/(Ni6/Co1.8)₃/Co5/Ru4/Co5/Mo2/ CoFeB4/Fe5/MgO/free layer/Mo20/Ta15/Ru100 stack annealed at 400° C. for 140 min. Free Layer Total FL Hk MR ratio A = Hk × Rel. (Total thickness = 12 Angstroms) FeCoB type (kOe) (%) MR ratio merit Comp. Ex. 1 Fe₆₀Co₂₀B₂₀12 Fe₆₀Co₂₀B₂₀ 1LR 7.5 98 735 0 Comp. Ex. 2 Fe₇₀Co₃₀ Fe₇₀Co₃₀ 1LR 7.0 90 630 0 Emb. 1 Fe₇₇Co₇B₁₆12 Fe₇₇Co₇B₁₆ 1LR 9.5 115 1093 1 Comp. Ex. 3 Fe8/Fe₆₀Co₂₀B₂₀4 Fe_(86.7)Co_(6.7)B_(6.7) 2LR 3.5 120 420 0 Emb. 1 Fe₇₀Co₃₀8/Fe₆₀Co₂₀B₂₀4 Fe_(66.7)Co_(6.7)B_(26.7) 2LR 9.6 108 1037 1 Emb. 1 Fe₇₀Co₃₀7/Fe₆₀Co₂₀B₂₀5 Fe_(65.8)Co_(8.3)B_(25.8) 2LR 9.6 123 1181 2 Comp. Ex. 4 Fe₆₀Co₂₀B₂₀4/Fe8 Fe_(86.7)Co_(6.7)B_(6.7) 2LR 4.0 55 220 0 Emb. 1 Fe₆₀Co₂₀B₂₀4/Fe₇₀Co₃₀8 Fe_(66.7)Co_(6.7)B_(26.7) 2LR 9.2 130 1196 2 Comp. Ex. 5 Fe4/Fe₆₀Co₂₀B₂₀4/Fe4 Fe₈₈Co₆B₆ 3LR 3.5 110 385 0 Emb. 2 Fe₇₀B₃₀4/Fe₆₀Co₂₀B₂₀4/Fe4 Fe_(76.7)Co_(6.7)B_(16.7) 3LR 9.4 139 1307 4 Emb. 2 Fe₇₀B₃₀4/Fe₆₀Co₂₀B₂₀4/Fe₉₀B₁₀4 Fe_(73.3)Co_(6.7)B₂₀ 3LR 9.3 137 1274 3 Emb. 2 Fe₇₀B₃₀4/Fe₆₀Co₂₀B₂₀4/Fe₈₅B₁₅4 Fe_(71.7)Co_(6.7)B_(21.7) 3LR 9.2 130 1196 2 Emb. 2 Fe₇₀B₃₀4/Fe₆₀Co₂₀B₂₀4/Fe₈₀B₂₀4 Fe₇₀Co_(6.7)B_(23.3) 3LR 9.0 131 1179 2 Emb. 2 Fe₇₀B₃₀4/Fe₆₀Co₂₀B₂₀4/Fe₇₀B₃₀4 Fe_(66.7)Co_(6.7)B_(26.7) 3LR 9.0 133 1197 2 Comp. Ex. 6 Fe4/Fe₆₀Co₂₀B₂₀4.6/Fe3.4 Fe_(84.7)Co_(7.7)B_(7.7) 3LR 3.5 110 385 0 Emb. 2 Fe₇₀B₃₀4/Fe₆₀Co₂₀B₂₀4.6/Fe3.4 Fe_(74.7)Co_(7.7)B_(17.7) 3LR 10.4 136 1414 5 Emb. 2 Fe₇₀B₃₀4/Fe₆₀Co₂₀B₂₀4.6/Fe₇₀B₃₀3.4 Fe_(66.2)Co_(7.7)B_(26.2) 3LR 9.0 130 1170 2 Comp. Ex. 7 Fe4/Fe₆₀Co₂₀B₂₀3.4/Fe4.6 Fe_(88.7)Co_(5.7)B_(5.7) 3LR 4.5 92 414 0 Emb. 2 Fe₇₀B₃₀4/Fe₆₀Co₂₀B₂₀3.4/Fe4.6 Fe_(78.7)Co_(5.7)B_(15.7) 3LR 9.0 133 1197 2 Emb. 2 Fe₇₀B₃₀4/Fe₆₀Co₂₀B₂₀3.4/Fe₇₀B₃₀4.6 Fe_(67.2)Co_(5.7)B_(27.2) 3LR 9.6 124 1190 2

Trilayer configurations from our prior p-MTJ development studies are listed as Fe4/Fe₆₀Co₂₀B₂₀4/Fe4 (Comp. Ex. 5), Fe4/Fe₆₀Co₂₀B₂₀4.6/Fe3.4 (Comp. Ex. 6), and Fe4/Fe₆₀Co₂₀B₂₀3.4/Fe4.6 (Comp. Ex. 7). Again, there is no improvement over the baseline results in Comp. Ex. 1 and 2. In comparison, all Embodiment 2 trilayer examples have A results above 1000, and in several cases, have an A value substantially higher than the Embodiment 1 (single layer or bilayer) configurations. For instance, the Fe₇₀B₃₀4/Fe₆₀Co₂₀B₂₀4/Fe4 and Fe₇₀B₃₀4/Fe₆₀Co₂₀B₂₀4.6/Fe3.4 examples according to the present disclosure have the best A results of 1307 and 1414, respectively. The latter is almost 2× higher than the Comp. Ex. 1 baseline value of 735. The Fe₇₀B₃₀4/Fe₆₀Co₂₀B₂₀4/Fe₉₀B₁₀4 trilayer also provides enhanced A results above 1200.

The results from Table 1 are displayed in bar chart form in FIG. 9. In summary, single layer or bilayer configurations having a Fe_(x)Co_(y)B_(z) total free layer composition where x is 66-80, y is 5-9, z is 15-28, and x+y+z=100 provide A results between 1000 and 1200, but the most desirable A results (1170-1414) are generated by trilayers with the Fe_(x)Co_(y)B_(z) composition. All compositions shown in Table 1 and in FIG. 9 are free layers as deposited and do not account for any M elements that may have diffused into the free layer during p-MTJ fabrication.

FIG. 10 is a FeCoB alloy graph that shows the preferred region A comprised of solid circles for achieving RA product <5 ohm/μm², MR ratio >100%, and thermal stability to 400° C. Note that switching voltage was not measured since the p-MTJ stacks were not patterned. However, Vc is expected to be <0.15V (DC) in view of p-MTJ stacks with a total FL composition of Fe_(x)Co_(y)B_(z) that have been patterned and characterized in other experiments that are not reported here. Outlying regions with open circles contain comparative example configurations shown in Table 1. In review, the comparative examples fail to provide desirable A values because Hk is degraded due to free layer intermixing with the Mo Hk enhancing layer. In general, MR ratio is below 100% in the outlying regions to further reduce the A result.

As mentioned earlier, free layer 14 in FIG. 1 and FIG. 2 may have a thickness from 8 to 15 Angstroms in either a single layer (as deposited) or triple layer configuration. Table 2 shows possible thicknesses of each layer in a Fe₇₀B₃₀/Fe₆₀Co₂₀B₂₀/Fe trilayer configuration that conforms to the Fe_(x)Co_(y)B_(z) total free layer composition according to an embodiment of the present disclosure.

TABLE 2 Trilayer stacks with thickness from 8 to 15 Angstroms, and total FL composition Fe_(x)Co_(y)B_(z) where x = 66-80, y = 5-9, z = 15-28 and x + y + z = 100. Total FL thickness FL 14-1 FL 14-2 FL 14-3 Fe_(x)Co_(y)B_(z) 15 Fe₇₀B₃₀ 5 Fe₆₀Co₂₀B₂₀ 5 Fe 5 Fe_(76.7)Co_(6.7)B_(16.7) Angstroms 14 Fe₇₀B₃₀ 5 Fe₆₀Co₂₀B₂₀ 5 Fe 4 Fe_(75.0)Co_(7.1)B_(17.9) Angstroms 13 Fe₇₀B₃₀ 4 Fe₆₀Co₂₀B₂₀ 5 Fe 4 Fe_(75.4)Co_(7.7)B_(16.9) Angstroms 12 Fe₇₀B₃₀ 3.5 Fe₆₀Co₂₀B₂₀ 4.5 Fe 4 Fe_(76.3)Co_(7.5)B_(16.3) Angstroms 11 Fe₇₀B₃₀ 3.5 Fe₆₀Co₂₀B₂₀ 4 Fe 3.5 Fe_(75.9)Co_(7.3)B_(16.8) Angstroms 10 Fe₇₀B₃₀ 3.5 Fe₆₀Co₂₀B₂₀ 3.5 Fe 3 Fe_(75.5)Co_(7.0)B_(17.5) Angstroms 9 Fe₇₀B₃₀ 3 Fe₆₀Co₂₀B₂₀ 3 Fe 3 Fe_(76.7)Co_(6.7)B_(16.7) Angstroms 8 Fe₇₀B₃₀ 2.5 Fe₆₀Co₂₀B₂₀ 3 Fe 2.5 Fe_(75.8)Co_(7.5)B_(16.9) Angstroms

Table 3 shows possible thicknesses of each layer in a Fe₇₀B₃₀/Fe₆₀Co₂₀B₂₀/Fe₇₀B₃₀ trilayer configuration that conforms to the Fe_(x)Co_(y)B_(z) total free layer composition according to an embodiment of the present disclosure.

TABLE 3 Trilayer stacks with thickness from 8 to 15 Angstroms, and total FL composition Fe_(x)Co_(y)B_(z) where x = 66-80, y = 5-9, z = 15-28 and x + y + z = 100. Total FL thickness FL 14-1 FL 14-2 FL 14-3 Fe_(x)Co_(y)B_(z) 15 Angstroms Fe₇₀B₃₀ 5 Fe₆₀Co₂₀B₂₀ 5 Fe₇₀B₃₀ 5 Fe_(66.7)Co_(6.7)B_(26.7) 14 Angstroms Fe₇₀B₃₀ 5 Fe₆₀Co₂₀B₂₀ 5 Fe₇₀B₃₀ 4 Fe_(66.4)Co_(7.1)B_(26.4) 13 Angstroms Fe₇₀B₃₀ 4 Fe₆₀Co₂₀B₂₀ 5 Fe₇₀B₃₀ 4 Fe_(66.2)Co_(7.7)B_(26.2) 12 Angstroms Fe₇₀B₃₀ 3.5 Fe₆₀Co₂₀B₂₀ 4.5 Fe₇₀B₃₀ 4 Fe_(66.3)Co_(7.5)B_(26.3) 11 Angstroms Fe₇₀B₃₀ 3.5 Fe₆₀Co₂₀B₂₀ 4 Fe₇₀B₃₀ 3.5 Fe_(66.4)Co_(7.3)B_(26.4) 10 Angstroms Fe₇₀B₃₀ 3.5 Fe₆₀Co₂₀B₂₀ 3.5 Fe₇₀B₃₀ 3 Fe_(66.5)Co_(7.0)B_(26.5)  9 Angstroms Fe₇₀B₃₀ 3 Fe₆₀Co₂₀B₂₀ 3 Fe₇₀B₃₀ 3 Fe_(66.7)Co_(6.7)B_(26.7)  8 Angstroms Fe₇₀B₃₀ 2.5 Fe₆₀Co₂₀B₂₀ 3 Fe₇₀B₃₀ 2.5 Fe_(66.3)Co_(7.5)B_(26.3)

A sequence of steps in FIGS. 11-13 show one process flow for forming a p-MTJ cell having a free layer 14 formed between a tunnel barrier layer 13, and a Hk enhancing layer 17 that is W, Mo, Mo alloy or a W alloy. Referring to FIG. 11, seed layer 11, reference layer 12, and tunnel barrier 13 are sequentially formed on bottom electrode 10 by conventional methods. Thereafter, free layer 14 having top surface 14 t is formed with sequential deposition of a FeB layer 14-1, FeCoB layer 14-2, and Fe or FeB layer 14-3 explained previously. All free layers are sputter deposited within a chamber having a base pressure of 5×10⁻⁸ to 5×10⁻⁹ torr, and typically using a sputter gas that is Ar. Preferably, layer 14-2 comprises more Co (higher Co content) than in layer 14-1 or in layer 14-3. Moreover, layer 14-3 preferably comprises a higher Fe content than in layer 14-2, and a B content ≤30 atomic %.

Referring to FIG. 12, a Hk enhancing layer 17 made of Mo, W, W alloy, or a Mo alloy may be sputter deposited on top surface 14 t in the same chamber used for depositing free layer 14. Thereafter, hard mask 16 with top surface 16 t is deposited on the Hk enhancing layer.

Referring to FIG. 13, a photoresist layer is coated on top surface 16 t and patterned by a conventional photolithography technique to yield a pattern comprised of island 30 with sidewall 30 s and a critical dimension (CD)=d in the y-axis direction. Note that a dielectric anti-reflective coating (DARC) or bottom anti-reflective coating (BARC) known in the art is generally formed between top surface 16 t and the photoresist layer to improve the process window and CD uniformity in a plurality of islands (not shown) across the substrate (wafer) but is not shown in this illustration. In some embodiments, the CD is also formed in the x-ax is direction to give a circular island shape from a top-down view. However, the CD in the x-axis direction may be different from d so that the island has an elliptical or polygonal shape from a top-down perspective.

One or more reactive ion etch (RIE) steps are employed to transfer the photoresist sidewall through the p-MTJ layers, and stop on top surface 10 t of the bottom electrode 10 as depicted in FIG. 1. As a result, sidewall 1 s on p-MTJ 1 is formed as a extension of sidewall 30s. The photoresist island is removed during the etch transfer and hard mask 16 ensures that the shape integrity (CD) of the original island shape 30 is preserved in the resulting p-MTJ cell. An ion beam etch may be used to remove RIE residue before a subsequent encapsulation layer (not shown) is deposited to insulate p-MTJ 1 from adjacent p-MTJ cells. A first anneal at >380° C. may be performed before the photoresist is coated and patterned. Furthermore, one or more processing steps including anneals at temperatures >380° C. may occur after p-MTJ 1 is formed according to various embodiments of the present disclosure. It is believed that the free layer will become crystalline after annealing in all embodiments considering the iron rich content of all layers in single layer, bilayer, and trilayer configurations described herein. Accordingly, the crystalline free layer should enable good lattice matching with a MgO tunnel barrier layer and with the Hk enhancing layer, which both have a body centered cubic (bcc) crystal structure after annealing.

Referring to FIG. 14, a process flow diagram is provided for an alternative embodiment where a single free layer with a Fe_(x)Co_(y)B_(z) composition where x is 66-80, y is 5-9, z is 15-28, and x+y+z=100 is formed between a tunnel barrier layer and a Hk enhancing layer. In the exemplary embodiment that relates to formation of a p-MTJ stack of layers with a bottom spin valve configuration, a p-MTJ stack of layers is provided with an uppermost tunnel barrier layer in step 70. Thereafter, in step 71, a Fe_(x)Co_(y)B_(z) free layer is deposited on the tunnel barrier layer. An Hk enhancing layer such as W, Mo, W alloy, or a Mo alloy, and an optional hard mask are sequentially formed on the free layer in step 72. Finally, the p-MTJ stack is annealed at a temperature >380° C. in step 73 so that the free layer may segregate into multiple sub-layers, and may absorb one or more M elements described previously. Alternatively, the sequence of steps is reversed so that the free layer is deposited on the Hk enhancing layer, and then the tunnel barrier is formed on the free layer when forming a top spin valve configuration. All of the aforementioned steps may be carried out within various chambers of a sputter deposition tool.

All of the embodiments described herein may be incorporated in a manufacturing scheme with standard tools and processes. P-MTJ cells formed according to preferred embodiments disclosed herein have a RA product below 5 ohm/μm², MR ratio >100%, Vc<0.15V (DC), and sufficient Hk to provide thermal stability to 400° C. process temperatures. We believe overall p-MTJ performance is an improvement over the prior art and thereby enables higher process yields of advanced product nodes such 64 Mb and 256 Mb STT-MRAM technology, and related spintronic devices where switching current, RA value, MR ratio, and thermal stability are all critical parameters.

While the present disclosure has been particularly shown and described with reference to, the preferred embodiment thereof, it will be understood by those skilled in the art that various changes in form and details may be made without departing from the spirit and scope of this disclosure. 

We claim:
 1. A perpendicularly magnetized magnetic tunnel junction (p-MTJ) formed in a memory device, comprising: (a) a reference layer (RL) with a fixed magnetization oriented in a direction perpendicular to a surface thereof; (b) a free layer (FL) comprised of at least Co, Fe, and B in a composition that is Fe_(x)Co_(y)B_(z) where x is 66-80, y is 5-9, z is 15-28, x+y+z=100, and with a magnetization oriented perpendicular to first and second surfaces thereof, and wherein the FL magnetization may be switched from a direction parallel to the RL direction to an anti-parallel direction to the RL fixed magnetization; (c) a tunnel barrier layer comprised of one or more metal oxides formed between the first surface of the free layer and the reference layer; and (d) a Hk enhancing layer comprised of W, Mo, or alloys thereof and adjoining the second surface of the free layer that is opposite to the first surface wherein the Hk enhancing layer induces perpendicular magnetic anisotropy (PMA) at an interface with the second surface.
 2. The p-MTJ of claim 1 further comprised of a seed layer as a bottommost layer that contacts the reference layer, and an uppermost hard mask formed on the Hk enhancing layer to give a bottom spin valve configuration.
 3. The p-MTJ of claim 1 further comprised of a seed layer as a bottommost layer that contacts the Hk enhancing layer, and an uppermost hard mask formed on the reference layer to give a top spin valve configuration.
 4. The p-MTJ of claim 1 wherein the free layer is a single layer.
 5. The p-MTJ of claim 1 wherein the free layer has a bilayer configuration that is a FeB/FeCoB stack or a FeCoB/FeB stack of layers such that a total composition of the free layer is Fe_(x)Co_(y)B_(z).
 6. The p-MTJ of claim 1 wherein the free layer is crystalline and has lattice matching with the tunnel barrier layer and Hk enhancing layer each of which have a body centered cubic (bcc) crystalline structure.
 7. The p-MTJ of claim 1 wherein the memory device is a magnetic random access memory (MRAM) or a spin torque (STT)-MRAM.
 8. The p-MTJ of claim 1 wherein the free layer is further comprised of one or more M elements where M is oxygen, nitrogen, or a metal from a p-MTJ layer that diffuses into the free layer during p-MTJ fabrication to give a free layer composition that is (Fe_(x)Co_(y)B_(z))_(w)M_(100-w) where w is >90 atomic %.
 9. A perpendicularly magnetized magnetic tunnel junction (p-MTJ), comprising: (a) a reference layer (RL) with a fixed magnetization oriented in a direction perpendicular to a surface thereof; (b) a tunnel barrier layer comprised of one or more metal oxides formed between a first surface of a free layer and the reference layer; (c) a Hk enhancing layer comprised of W, Mo, or alloys thereof and adjoining a second surface of the free layer that is opposite to the first surface wherein the Hk enhancing layer induces perpendicular magnetic anisotropy (PMA) at an interface with the second surface; and (d) the free layer (FL) with a trilayer configuration (FL1/FL2/FL3) comprised of at least Co, Fe, and B in a total composition that is Fe_(x)Co_(y)B_(z) where x is 66-80, y is 5-9, z is 15-28, and x+y+z=100, and with a magnetization oriented perpendicular to the first and second surfaces thereof, wherein the FL magnetization may be switched from a direction parallel to the RL direction to an anti-parallel direction to the RL magnetization, the FL comprises; (1) a first layer (FL1) that is FeB and which contacts the tunnel barrier layer; (2) a second (middle) layer (FL2) that is FeCoB, and wherein FL2 has a higher Co content than FL1 and FL3; and (3) a third layer (FL3) that is Fe or FeB and which adjoins the Hk enhancing layer, and wherein FL3 has a higher Fe content than FL2.
 10. The p-MTJ of claim 9 wherein the free layer has a thickness from about 8 to 15 Angstroms.
 11. The p-MTJ of claim 9 further comprising a seed layer as a bottommost layer that contacts the reference layer, and a hard mask that is an uppermost layer formed on the Hk enhancing layer to give a bottom spin valve configuration.
 12. The p-MTJ of claim 9 further comprising a seed layer as a bottommost layer that contacts the Hk enhancing layer, and a hard mask that is an uppermost layer formed on the reference layer to give a top spin valve configuration.
 13. The p-MTJ of claim 9 wherein the free layer is crystalline and has lattice matching with the tunnel barrier layer and Hk enhancing layer each of which have a body centered cubic (bcc) crystalline structure.
 14. The p-MTJ of claim 9 wherein the Mo alloy is MoW or MoD, and the W alloy is WD where D is one of Nb, Ti, Ta, Zr, Hf, V or Cr, and D is less than 20 atomic %.
 15. The p-MTJ of claim 9 wherein the Hk enhancing layer has a thickness from about 10 to 50 Angstroms.
 16. The p-MTJ of claim 9 wherein the tunnel barrier layer is one of MgO, TiOx, AlTiO, MgZnO, Al₂O₃, ZnO, ZrOx, HfOx, or MgTaO, or a lamination of one or more of the aforementioned metal oxides.
 17. The p-MTJ of claim 9 wherein the free layer is further comprised of one or more M elements where M is oxygen, nitrogen, or a metal from a p-MTJ layer that diffuses into the free layer during p-MTJ fabrication to give a free layer composition that is (Fe_(x)Co_(y)B_(z))_(w)M_(100-w) where w is >90 atomic %.
 18. A method of forming a perpendicular magnetized magnetic tunnel junction (p-MTJ) comprised of a reference layer (RL) with a fixed magnetization oriented perpendicular to a surface thereof, a free layer with a magnetization that is parallel or anti-parallel to the RL magnetization, and a tunnel barrier layer between the reference layer and free layer, comprising: (a) providing a stack of layers having an uppermost layer that is a tunnel barrier layer and wherein the tunnel barrier layer is formed on the RL; (b) depositing a free layer on the tunnel barrier layer wherein the free layer comprises at least Fe, Co, and B in a composition that is Fe_(x)Co_(y)B_(z) where x is 66-80, y is 5-9, z is 15-28, and x+y+z=100, and wherein the free layer is formed by a process comprising; (1) depositing a first layer (FL1) that is FeB on the tunnel barrier layer; (2) depositing a second layer (FL2) that is FeCoB on FL1 wherein FL2 has a higher Co content than FL1; and (3) depositing a third layer (FL3) that is Fe or FeB on FL2 wherein FL3 has a higher Fe content than FL2; (c) depositing a Hk enhancing layer that is W, Mo, a W alloy, or a Mo alloy on FL3 to give a p-MTJ stack of layers having a RL/tunnel barrier/FL/Hk enhancing layer configuration; and (d) performing an annealing step at a temperature >380° C.
 19. The method of claim 18 wherein the annealing step is performed before or after the p-MTJ stack of layers is patterned into a plurality of p-MTJ cells.
 20. The method of claim 18 wherein the free layer has a thickness from about 8 to 15 Angstroms.
 21. The method of claim 18 wherein all layers in the p-MTJ stack are formed in one sputter deposition tool.
 22. The method of claim 18 wherein the Hk enhancing layer has a thickness from about 10 to 50 Angstroms.
 23. The method of claim 18 wherein the free layer further comprises one or more M elements after depositing the Hk enhancing layer and performing the annealing step, wherein M is oxygen, nitrogen, or a metal from another p-MTJ layer that diffused into the free layer to give a free layer composition that is (Fe_(x)Co_(y)B_(z))_(w)M_(100-w) where w is >90 atomic %.
 24. A method of forming a perpendicular magnetized magnetic tunnel junction (p-MTJ) comprised of a reference layer (RL) with a fixed magnetization oriented perpendicular to a surface thereof, a free layer with a magnetization that is parallel or anti-parallel to the RL magnetization, and a tunnel barrier layer between the reference layer and free layer, comprising: (a) providing a Hk enhancing layer that is W, Mo, a W alloy, or Mo alloy; (b) depositing a free layer with a FL3/FL2/FL1 trilayer configuration on the Hk enhancing layer wherein the free layer comprises at least Co, Fe, and B in a total composition that is Fe_(x)Co_(y)B_(z) in which x is 66-80, y is 5-9, z is 15-28, and x+y+z=100, and wherein the free layer is formed by a process comprising; (1) depositing layer FL3 that is Fe or FeB on the Hk enhancing layer wherein FL3 has a higher Fe content than in FL2; (2) depositing layer FL2 that is FeCoB on FL3 wherein FL2 has a higher Co content than in FL1; and (3) depositing layer FL1 that is FeB on FL2; (c) sequentially forming a tunnel barrier layer and the RL on FL1; and (d) performing an annealing step at a temperature >380° C.
 25. The method of claim 24 wherein the annealing step is performed before or after the p-MTJ stack of layers is patterned into a plurality of p-MTJ cells.
 26. The method of claim 24 wherein the free layer has a thickness from about 8 to 15 Angstroms.
 27. The method of claim 24 wherein all layers in the p-MTJ stack are formed in one sputter deposition tool.
 28. The method of claim 24 wherein the Hk enhancing layer has a thickness from about 10 to 50 Angstroms.
 29. The method of claim 24 wherein the free layer further comprises one or more M elements after performing the annealing step, wherein M is oxygen, nitrogen, or a metal from another p-MTJ layer that diffused into the free layer to give a free layer composition that is (Fe_(x)Co_(y)B_(z))_(w)M_(100-w) where w is >90 atomic %.
 30. A method of forming a perpendicular magnetized magnetic tunnel junction (p-MTJ) wherein a stack of layers has a Hk enhancing layer/free layer (FL) or FL/Hk enhancing layer configuration and where a tunnel barrier layer is formed between the FL and a reference layer (RL); comprising: (a) providing the stack having the Hk enhancing layer/FL or FL/Hk enhancing layer configuration where the Hk enhancing layer is W, Mo, a W alloy, or a Mo alloy, and wherein the FL has a magnetization that is perpendicular to a surface thereof and is switchable to a direction that is parallel or anti-parallel to a fixed reference layer magnetization, and wherein the FL is comprised of at least Fe, Co, and B in a composition that is Fe_(x)Co_(y)B_(z) in which x is 66-80, y is 5-9, z is 15-28, and x+y+z=100; and (b) performing an annealing step at a temperature >380° C.
 31. The method of claim 30 wherein the FL/Hk enhancing layer configuration further comprises a seed layer as the bottommost layer that contacts the RL, and a hard mask as the uppermost layer formed on the Hk enhancing layer to give a bottom spin valve configuration that has a seed layer/RL/tunnel barrier/FL/Hk enhancing layer/hard mask stack of layers.
 32. The method of claim 30 wherein the configuration further comprises a seed layer as the bottommost layer that contacts the Hk enhancing layer, and a hard mask as the uppermost layer formed on the RL to give a top spin valve configuration that has a seed layer/Hk enhancing layer/FL/tunnel barrier/RL/hard mask stack of layers.
 33. The method of claim 30 wherein the free layer has a thickness from about 8 to 15 Angstroms.
 34. The method of claim 30 wherein the annealing is performed before or after the stack of layers is patterned to form a plurality of p-MTJ cells.
 35. The method of claim 30 wherein the free layer further comprises one or more M elements after performing the annealing step, wherein M is oxygen, nitrogen, or a metal from another p-MTJ layer that diffused into the free layer to give a free layer composition that is (Fe_(x)Co_(y)B_(z))_(w)M_(100-w) where w is >90 atomic %. 